A flexible capita deve esse umida?

Quandu custruite revestimenti impermeabili flessibili (cum'è i rivestimenti impermeabili basati in cimentu polimeru, polyurethane waterproof coatings, ecc.), the wetness requirements of the base surface need to be determined according to the specific material type and construction environment, but generally follow the following principles:

1. Cement-based flexible waterproofing (such as JS waterproof coatings, K11 waterproof slurry, ecc.)

   • The base surface needs to be moist but without obvious water:This type of material usually requires the base surface to remain moist but without water accumulation (commonly known as “dry surface and wet inside”).

   • A moist base surface helps the waterproof slurry to better bond with the base layer, and prevents the dry base surface from absorbing moisture too quickly, causing the coating to crack or powder.

     Operation suggestions: Sprinkle water to moisten the base surface before construction, è appricà dopu chì ùn ci sò micca gocce d'acqua evidenti nantu à a superficia.

2. Impermeabilizzazione flessibile in poliuretano (cumpunente unicu/doppiu)

   • A superficia di a basa deve esse secca:I rivestimenti di poliuretano sò sensibili à l'umidità, è a superficia di a basa deve esse ben secca (u cuntenutu di umidità hè generalmente necessariu per esse ≤8%), altrimenti bolle è delaminazione sò prubabilmente accade.

   • Eccezzioni: Certi poliuretani mudificati (cum'è i tipi di cura di l'umidità) pò esse appiicata nantu à sustrati umidi, ma deve esse operatu strettamente secondu l'istruzzioni di u produttu.

3. Precauzioni generale

   • U trattamentu di basa hè una priorità:Ch'ella sia umita o secca, u sustrato deve esse fermu, pianu, senza oliu è materiali sciolti. I cracks è i buchi deve esse chini prima cù mortar di riparazione.

   • A temperatura ambientale è l'umidità:Avoid construction in high temperature and windy weather to prevent water from evaporating too quickly (cement-based materials) or abnormal curing (polyurethane).

   • Product instructions shall prevail:Different brands and types of waterproof materials may have different requirements, so be sure to follow the construction guide provided by the manufacturer.

Summary suggestions

• Cement-based flexible waterproofing: The substrate is more reliable to wet, but there is no visible water on the surface.

• Polyurethane waterproofing: The substrate must be dry.

• Test method: Use absorbent paper to stick to the substrate. If there is no obvious water stain, it is in the “no visible water” state

• Be sure to confirm the material properties before construction and do a small area test to ensure the bonding effect!

If the base surface is not moistened as required when constructing flexible waterproof coatings (especially cement-based waterproof materials), the following problems may occur:

1. Cement-based flexible waterproofing (such as JS/K11 coatings)

   • Decreased adhesio

     • The dry base surface will quickly absorb the moisture in the waterproof slurry, resulting in the coating being unable to fully hydrate, and the adhesion to the base layer is not strong, which is prone to hollowing and delamination.

     • Phenomenon: After completion, the coating may be torn or knocked by hand, and the entire piece may peel off.

2. Cracks or powdering of the coating

   • After excessive moisture is absorbed, the coating cannot complete the curing reaction due to lack of water, and the surface dries too quickly, forming cracks or loose powder layers.

3. Failure of waterproof performance

   • Micro crepe è cavità formanu canali di filtrazione d'acqua, è l'acqua pò penetrà da i punti debuli, pruvucannu u fallimentu generale di u sistema impermeabile

4. Rivestimenti impermeabili in poliuretano

   • Meno impattu da u sustrato seccu

     • U poliuretanu stessu precisa un sustrato seccu, ma se u sustrato hè troppu seccu è poroso (cum'è un vechju sustrato di cimentu), pò esse necessariu di prima applicà un primer (cum'è un primer epoxy) per sigillà i pori, altrimenti:

     • U revestimentu penetrarà troppu in u sustrato, risultatu in un spessore insufficiente

     • Se u polu nantu à u sustrato ùn hè micca pulitu, l'aderenza serà ridutta.

5. Circunstanze particulare (alta temperatura / ambiente ventu)

   • Ancu s'è u materiale stessu ùn deve micca un altu cuntenutu di umidità (cum'è certi rivestimenti acrilichi), in tempu caldu è ventu, un sustrato seccu accelerà l'evaporazione di l'umidità da u revestimentu, risultatu in:

   • Retrazione è cracking di u revestimentu;

   • Formazione di film discontinuu è pinholes

Cumu rimedià un sustrato unmoistened?

1. Impermeabilizzazioni à base di cimentu: Ferma immediatamente a custruzione, Spray acqua nantu à a zona dipinta per mantenimentu (se l'impostazione iniziale ùn hè micca cumpleta), o scrape it off and re-humidità u sustrato prima di a custruzzione

2. Polyurethane waterproofing: Assicuratevi chì u sustrato hè seccu è senza polvera, è pulisce è applicà un primer speciale se ne necessariu

Cunclusioni chjave

• Impermeabilizzazioni à base di cimentu: Ùn wetting a superficia di basa ≈ “lassendu u rivestimentu mori di sete”, dannu direttamente u ligame è a forza

• Altri materiali: A superficia di a basa deve esse trattata strettamente secondu i bisogni di u produttu, seccu ≠ senza trattamentu (a pulizia è u nivellu sò sempre necessarii

• Cunsigliu ultimu: Before construction, wipe the base surface with a wet sponge to achieve a “saturated dry surface” state (no visible water, slightly cool to the touch) for the safest.